Degradation of carbon negative electrodes in lithium-ion batteries
Abstract/Contents
- Abstract
- The graphitic negative electrode is widely used in today's commercial lithium-ion batteries. However, its lifetime is limited by a number of degradation modes, particularly growth of the solid electrolyte interphase (SEI), lithium plating, and electrode inactivation. Two major challenges to better batteries are the range of length scales (nanometers to centimeters) over which degradation modes occur, as well as slow development times. In this thesis, I overcome these challenges by studying the degradation of carbon electrodes in both model systems and commercial devices and by using machine learning methods for accelerated battery optimization. First, I study SEI growth on carbon black via microscopy, electrochemistry, and modeling. I first use cryogenic transmission electron microscopy (cryo-EM) to image the SEI on carbon black and track its evolution during cycling. I observe an evolution of inorganic components in thin (~2 nm), primary SEI directly interfaced to the carbon black, as well as deposits of SEI that span hundreds of nanometers. I then electrochemically measure the dependence of SEI growth on potential, current magnitude, and current direction during galvanostatic cycling. I find that SEI growth strongly depends on all three parameters; most notably, SEI growth rates increase with nominal C rate and are significantly higher on lithiation than on delithiation. Finally, I model the SEI as a mixed ionic-electronic conductor, where the ionic concentration modulates the electronic conductivity. This model can account for the previously observed directional dependence. This work illustrates the MIEC-like nature of the SEI on carbonaceous anodes and illustrates the strong coupling between charge storage (i.e. intercalation) and SEI growth. Second, I characterize the cell-level degradation of commercial lithium iron phosphate (LFP)/graphite cylindrical cells during fast charging. I find that the graphite electrode exhibits significant and highly heterogeneous degradation during fast charging, with large ionically inactive regions located near the electrode tab. This ionic inactivation of the electrode appears to occur via large-scale SEI growth, preceding more conventional fast charging degradation modes such as lithium plating. Third, I optimize a six-step fast-charging protocol that achieves 80% state of charge in ten minutes on commercial LFP/graphite cylindrical cells. I first develop a machine learning algorithm that uses cycling data from the first 100 cycles to predict cycle lives that reach up to 2300 cycles with ~9% error. Then, I use an optimal experimental design methodology for fast-charging protocol optimization, with two key elements to reduce the optimization cost: early prediction of failure, which reduces the cost per experiment, and adaptive Bayesian multi-armed bandits, which reduces the number of experiments required. The fast charging protocols identified by this algorithm are unexpected given the battery literature. The combination of closed-loop optimization and early prediction illustrates the power of data-driven methods to accelerate the pace of scientific discovery.
Description
| Type of resource | text |
|---|---|
| Form | electronic resource; remote; computer; online resource |
| Extent | 1 online resource. |
| Place | California |
| Place | [Stanford, California] |
| Publisher | [Stanford University] |
| Copyright date | 2019; ©2019 |
| Publication date | 2019; 2019 |
| Issuance | monographic |
| Language | English |
Creators/Contributors
| Author | Attia, Peter Magdy |
|---|---|
| Degree supervisor | Chueh, William |
| Thesis advisor | Chueh, William |
| Thesis advisor | Cui, Yi, 1976- |
| Thesis advisor | Toney, Michael Folsom |
| Degree committee member | Cui, Yi, 1976- |
| Degree committee member | Toney, Michael Folsom |
| Associated with | Stanford University, Department of Materials Science and Engineering. |
Subjects
| Genre | Theses |
|---|---|
| Genre | Text |
Bibliographic information
| Statement of responsibility | Peter Magdy Attia. |
|---|---|
| Note | Submitted to the Department of Materials Science and Engineering. |
| Thesis | Thesis Ph.D. Stanford University 2019. |
| Location | electronic resource |
Access conditions
- Copyright
- © 2019 by Peter Magdy Attia
- License
- This work is licensed under a Creative Commons Attribution Non Commercial 3.0 Unported license (CC BY-NC).
Also listed in
Loading usage metrics...